退火温度对Nb＋Ti双稳铁素体不锈钢织构的影响  

Effect of Annealing Temperature on Texture of Nb+Ti Stabilized Ferritic Stainless Steel

作　　者：颜海涛[1,2] 毕洪运[2] 李鑫[2] 顾佳卿[2] 徐洲[1] 

机构地区：[1]上海交通大学材料科学与工程学院,上海200240 [2]宝钢股份研究院,上海201900

出　　处：《钢铁》2009年第6期69-72,共4页Iron and Steel

摘　　要：利用电子背散射衍射技术(EBSD)研究了不同退火温度对Nb+Ti双稳铁素体不锈钢织构的影响。结果表明,随着退火温度的升高,α织构逐渐减弱,γ织构逐渐增强,当退火温度为920℃时,α织构基本消失,材料以γ织构为主。对再结晶织构的形成机制的探讨认为,铁素体不锈钢具有较强的γ织构归因于"定向形核"和"选择生长"共同作用的结果。The effect of annealing temperature on texture of Nb＋Ti stabilized ferritic stainless steel was investigated by using Electron Back-scattered Diffraction （EBSD）. The results indicate that the amounts of α texture decreased, but γ texture increased with the increasing of annealing temperature. When the annealing temperature was 920℃, the α texture disappeared and the principal texture was γ texture. A possible formation mechanism of recrystallization texture was that the formation of γ texture in ferritic stainless steel attributed to the combined effect of ＂orientated nucleation＂ and ＂selective growth＂.

关 键 词：铁素体不锈钢 织构 电子背散射衍射技术 

分 类 号：TG142.71[一般工业技术—材料科学与工程]