PFBC-CC燃气透平叶片防护涂层热态筛选试验研究  

Experimental Research on Hot State Selections ofPFBCCC Gas Turbine Blades Coatings

作　　者：仲兆平[1] 戴锅生[1] 章名耀[1] 徐爱群[1] 王世栋[1] 

机构地区：[1]东南大学

出　　处：《燃烧科学与技术》1998年第2期113-120,共8页Journal of Combustion Science and Technology

摘　　要：ＰＦＢＣ－ＣＣ燃气透平叶片工作条件恶劣，通过施加防护涂层可有效地防止叶片腐蚀和磨蚀。本文叙述了１５ＭＷＰＦＢＣ－ＣＣ中试燃气透平叶片防护涂层动态筛选试验的情况。试验在一台材料腐蚀（磨蚀）试验装置上进行，分高、低温两个试验段，选择了３种工艺、１４种配方的涂层参加试验。运用ＳＥＭ、ＴＥＭ、ＸＲＤ、ＥＤＡＸ、ＡＥＳ等现代分析手段和腐蚀（磨蚀）机理对试验结果进行了详细的分析，筛选出的优秀涂层为：高温区ＣＲ１涂层，低温区ＣＲ９涂层。这些涂层已用于中试燃气透平叶片上。强化试验的腐蚀（磨蚀）机理为：腐蚀（磨蚀）交互作用，高温区为磨蚀增强的腐蚀过程，低温区为腐蚀增强的磨蚀过程。お? As　PFBCCC　gas　turbine　blades　work　in　adverse　circumstances,the　method　of　exerting　coating　is　applied　in　order　to　lighten　blade　corrosion　and　erosion.This　paper　presents　the　experiment　of　hot　state　selection　of　15　MW　PFBCCC　pilot　gas　turbine　blade　coatings.A　novel　test　facility　of　materials　corrosion/erosion　is　studied　and　manufactured　by　authors.This　facility　has　two　test　sections　that　are　high,low　temperature　sections.Coatings　of　3　technologies　and　14　prescriptions　are　tested　in　hot　sate　in　this　facility.Excellent　coatings　are　selected　through　analysis　with　some　modern　analysis　methods　such　as　SEM,TEM,XRD,EDAX,AES,etc.and　corrosion/erosion　theory.These　coatings　have　applied　in　the　gas　trubine　blades　of　the　15 MW　PFBCCC　pilot　plant.The　corrosion/erosion　mechanism　of　coatings　in　the　experimental　conditions　is　coaction　of　corrosion/erosion.It　is　erosionenhanced　corrosion　at　760 ℃,and　corrosionenhanced　erosion　at　590 ℃.

关 键 词：燃气轮机 叶片 涂层 腐蚀 腐蚀 PFBC-CC 

分 类 号：TM611.31[电气工程—电力系统及自动化] TK263.3[动力工程及工程热物理—动力机械及工程]