γ射线照射与非照射人肌腱生物力学的比较研究  

Biomechanical research on gamma irradiated versus nonirradiated human tendon

作　　者：潘丕春[1] 刘金钊[1] 孙康[1] 

机构地区：[1]青岛大学医学院附属医院关节外科,青岛266021

出　　处：《中国矫形外科杂志》2009年第13期1010-1012,共3页Orthopedic Journal of China

摘　　要：[目的]探讨目前国内外最普遍应用的"γ"射线照射消毒法对人肌腱生物力学的影响。[方法]将等长的24条肱二头肌肌腱长头配对分成两组,A组(12):非照射组,B组(12):经2.5Mrad"γ"射线照射组。采用WDW-3020电子万能材料试验机测定结构力学和材料力学。[结果]经拉伸实验后肌腱平均长度B组为A组的99.15%,最大拉长量为93.46%,刚度为95.27%,最大载荷能量为93.60%,最大应力为84.88%,最大应变为85.82%,弹性模量为90.40%,能量密度为66.73%,B组照射组与A组非照组比较P<0.05,有统计学意义,照射后生物力学各参数明显降低。[结论]"γ"射线照射消毒后肌腱强度明显降低,是否采用"γ"射线照射消毒同种异体组织有待于进一步研究。[ Objective ] To explore the change of biomechanics about human tendon with ＂γ＂ irradiated which was universal used by domestic and foreign. [ Methods ] Twenty - four upper limb tendon of human with the same length were divided into two groups, group A （ 12 ） ： nonirradiated group, group B （ 12 ） ： 2. 5 Mrad gamma irradiated group. Material properties and structural properties were determined with WDW- 3020 electron universal testing machine. E Results] The mean length of the tendon was 99.15% of control, the elongation to failure was 93.46%, the linear stiffness was 95.27%, the energy to maximum force was 93.60% , the maximum stress was 84. 88% , the strain to failure was 85.82% , the linear modulus was 90.40%, the strain energy density to maximum was 66. 73 %. Difference was noted after compared hetween group A and B （P 〈 0. 05 ） . All biomechanical parameter presented significantly decline after irradiated. [ Conclusion ] The tendon strength reduced obvi- ously after irradiated, it needs further studies whether disinfect allograft could be irradiated with Gamma radiation on clinical.

关 键 词：生物力学 人 交叉韧带 移植 同种异体 照射 肌腱 

分 类 号：R318.01[医药卫生—生物医学工程]