超韧PA6/ABS合金性能和断口形貌研究  

Mechanical Properties and Fracture of the Super-Tough PA6/ABS Alloy

作　　者：朱红[1,2] 郭建兵[1] 何敏[1] 陈兴江 秦舒浩[1] 

机构地区：[1]国家复合改性聚合物材料工程技术研究中心,贵州贵阳550014 [2]贵州科技工程职业学院,贵州贵阳550008 [3]贵州省工程复合材料中心,贵州贵阳550014

出　　处：《塑料》2009年第3期4-6,38,共4页Plastics

基　　金：国家科技支撑计划项目(2007BAB08B05);贵州省工业攻关项目〔黔科合GY字(2008)(3005)〕

摘　　要：以苯乙烯-马来酸酐共聚物(SMA)为增容剂,研究了SMA含量对PA6/ABS共混物力学性能和断口形貌的影响。实验结果表明:随着SMA含量的增加,PA6/ABS共混物的拉伸强度逐渐增加,冲击强度先增加,接着保持不变,后降低;PA6/ABS共混物冲击断面可分为裂纹稳定扩展区与快速扩展区,SMA质量含量超过临界值后稳定扩展区相对面积明显减少,且使稳定扩展区相对面积明显减少的SMA临界含量随着共混物中ABS含量增加而增加。PA6/ABS blends compatibilized with styrene-maleic anhydride （SMA） were prepared in a corotating twinscrew extruder with different blending procedure. A study on influence of SMA contents was conducted through observation of SEM. The results showed that tensile strength of PA6/ABS blends increased by adding SMA impact strength firstly increased, subsequently kept without change, lastly decreased. The impact fracture surface included stable crack propagation region and rapid propagation region. When the content of SMA over the critical value, the stable propagation region decreased significantly, and the critical value of the SMA increased with the increasing of ABS.

关 键 词：PA6 ABS 合金 性能 超韧 

分 类 号：TQ342.11[化学工程—化纤工业] TQ325.2