PUI／蒙脱土纳米复合材料的制备及其性能研究  

Preparation and Properties on PUI/MMT Nanocomposite

作　　者：王士财[1] 张晓东[1] 楼涛[1] 佘希林[1] 李志国[1] 

机构地区：[1]青岛大学化学化工与环境学院,山东青岛266071

出　　处：《塑料科技》2009年第7期47-50,共4页Plastics Science and Technology

摘　　要：考察了聚氨酯-异氰脲酸酯(PUI)的基础配方,采用原位聚合方法制备了PUI/蒙脱土(MMT)纳米复合材料,并研究了纳米蒙脱土(Nano-MMT)用量对复合材料性能的影响。结果表明:以n(NCO):n(OH)=10:1、DMP-30用量为2.5%的PUI配方为基础制备的PUI/MMT纳米复合材料的力学性能和热稳定性都得到显著提高,当Nano-MMT用量为3%时,复合材料的综合性能最优。The polyurethane-isocyurnate （PUI）/montmorillonite （MMT） nanocomposite was prepared by situ polymerization, on the basis of studying PUI fundamental formula and the effects of the Nano-MMT content on the properties of PUI/MMT nanocomposite were also studied. The results showed that the mechanical and thermal properties of PUI/MMT nanocomposite prepared with the PUI fundamental formula in which n（NCO）In（OH） ratio was 10：1, catalyst （DMP-30） was 2.5% and with Nano-MMT were greatly improved. And when Nano-MMT content was 3%, the general properties of composites were the best.

关 键 词：聚氨酯 异氰脲酸酯 纳米蒙脱土 制备 性能 

分 类 号：TB383.1[一般工业技术—材料科学与工程]