莲纤维脱胶漂白工艺  

Degumming and bleaching of lotus fiber

作　　者：张宏伟[1] 李永兰[1] 王明芳[1] 李南[1] 

机构地区：[1]常州纺织服装职业技术学院纺织化学工程系,江苏常州213164

出　　处：《印染》2009年第14期16-18,共3页China Dyeing and Finishing

基　　金：常州市新型纺织材料重点实验室建设项目(CM2008304);常州市科技局工业科技攻关计划项目(CE2007073)

摘　　要：以农业生产废弃的食用莲藕荷叶茎秆为原料,采用浸渍、剥取、二煮一漂的脱胶漂白前处理工艺,以制取莲纤维。通过正交试验,优化得第二次碱煮和漂白工艺条件:氢氧化钠14 g/L,100℃碱煮3.5 h;过氧化氢10 g/L,60℃漂白60 min。以此工艺制取的精制莲纤维线密度25.9 dtex,强度1.68 cN/dtex,强度变异系数46.4%,断裂伸长率6.68%,白度42.9%,具有一定的可纺性能。Lotus fiber was prepared with edible lotus stalk as raw material via river dipping, hand-stripping and two-scouring- one-bleaching processing. The second scouring and bleaching process was optimized by orthogonal experiments, and processing conditions were defined as follows： scouring with 14 g/L caustic soda at 100 ℃ for 3.5 hours; and bleaching with 10 g/L hydrogen peroxide at 60℃ for 60 minutes. The prepared lotus fiber featured fairly good spinability with mean linear density 25.9 dtex, relative strength 1.68 cN/dtex, relative strength variation coefficient 46.6%, and whiteness 42.9%.

关 键 词：脱胶 漂白 植物纤维 

分 类 号：TS192.7[轻工技术与工程—纺织化学与染整工程]