回火温度对GDL-1高强韧新材料断裂韧性的影响  

Impact of Tempering Temperature on Fracture Toughness of High Tenacious Steel(GDL-1)

作　　者：凌敏[1] 朱茂兰[2] 梁益龙[3] 

机构地区：[1]铜仁职业技术学院机电系,贵州铜仁554300 [2]江西理工大学应用科学学院,江西赣州341000 [3]贵州大学材料科学与冶金工程学院贵州省材料结构与强度重点实验室,贵州贵阳550003

出　　处：《物理测试》2009年第4期1-4,共4页Physics Examination and Testing

基　　金：贵州省创新基金(024015)

摘　　要：研究了在低温回火温度范围内，不同回火温度对新型高强韧微变形钢（GDL-1）断裂性能的影响，分析了7种不同热处理状态的断裂性能。结果表明，空冷状态的断裂韧度、冲击韧度要高于油淬状态，空冷后的残余奥氏体量高于油淬后的残留奥氏体量，此外低温回火改善钢的韧性，并使残余奥氏体的稳定性提高，从而使该钢在空冷250-300℃回火后具有良好的断裂韧性。The fracture toughness of new tiny deformation steel（GDL-1） are studied at seven different heat treatment temperatures. The results show that in air-cooled state the fracture toughness, impact toughness is higher than that in oil quenching state, The amount of residual austenite after air cooling is greater than the one after oil cooling. The toughness of steel and the stability of residual austenite are improved, by means of tempering at 250-300 ℃ fol- lowed by ari-cooling,resulting in good fracture toughness.

关 键 词：微变形 GDL-1 热处理 断裂韧性 空冷 

分 类 号：TG151[金属学及工艺—热处理]