原位生成法制备聚酯/钛系化合物杂化涂层基体  

Study on Polyester/Titanium Hybrid Coating Prepared by In-situ Fabrication Method

作　　者：董卫卫[1] 俞昊[1] 洪范[1] 孙宾[1] 朱美芳[1] 

机构地区：[1]东华大学纤维材料改性国家重点实验室,上海201620

出　　处：《上海涂料》2009年第7期10-12,共3页Shanghai Coatings

基　　金：上海市纳米专项(0652nm041)和Evonik Degussa联合支持

摘　　要：由原位生成法制备了聚酯/钛系化合物有机-无机杂化涂层基体,利用流变仪、扫描电子显微镜(SEM)、傅立叶变换红外光谱(FT-IR)测试了杂化涂层基体的性能。结果表明:聚酯/钛系化合物杂化涂层基体均一透明,钛系化合物均匀分布在涂膜中且与聚酯形成化学键结合。Polyester/titanium organic-inorganic hybrid coating was prepared by the method of in-situ fabrication (ISF). The properties of the hybrid coating were investigated by rheometer, SEM and FTIR respectively. The result showed that the uniform and transparent polyester/titanium hybrid coating was obtained. Titanium compounds uniformly distributed in coating and combined with polyester by chemical bonds.

关 键 词：原位生成法 聚酯 钛系化合物 有机-无机杂化 