Preparation and Characteristic of Self-regulation Water-transmitting Coating Fiber  

作　　者：张增志 

机构地区：[1]Research Institute of Ecological and Functional Materials,China University of Mining and Technology(Beijing)

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2009年第4期520-524,共5页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National High Technology Research and Development Program of China (2001AA322100);the Ministry of Education of Republic of China (106086);the Cooperation and Merger Found of Beijing ( ZH114140537)

摘　　要：Common clay, Kaolin and Bentonite were used as additives to prepare water-transmitting coating fiber, respectively, and the water-transmitting characteristic of coating fiber was studied. Different water-transmitting coating fibers were prepared by coating fiber using coating material with different mass proportions of additives to adhesive. And the coating materials were made from three kinds of inorganic clays as additives respectively and polyvinyl alcohol （PVA） as adhesive. Furthermore, the surface morphology and water-transmitting capacity of coating fiber were studied by SEM, Perkin Elmer Diamond SII thermal multi-analyzer and instrument for quick measurement moisture M30. The experimental results indicate that water-transmitting coating fibers made from three kinds of clays all have water-transmitting capacity. The surface of water-transmitting coating fiber prepared by common clay T is continuous and compact, and the water-transmitting effect is better than coating fibers made from other clays.Common clay, Kaolin and Bentonite were used as additives to prepare water-transmitting coating fiber, respectively, and the water-transmitting characteristic of coating fiber was studied. Different water-transmitting coating fibers were prepared by coating fiber using coating material with different mass proportions of additives to adhesive. And the coating materials were made from three kinds of inorganic clays as additives respectively and polyvinyl alcohol （PVA） as adhesive. Furthermore, the surface morphology and water-transmitting capacity of coating fiber were studied by SEM, Perkin Elmer Diamond SII thermal multi-analyzer and instrument for quick measurement moisture M30. The experimental results indicate that water-transmitting coating fibers made from three kinds of clays all have water-transmitting capacity. The surface of water-transmitting coating fiber prepared by common clay T is continuous and compact, and the water-transmitting effect is better than coating fibers made from other clays.

关 键 词：self-regulation water-transmitting coating fiber storage and controlled-release film composite film inorganic clay 

分 类 号：TQ340.1[化学工程—化纤工业]