降解性聚乙烯地膜的研制及其降解过程  

Preparation and Degradation of Degradable PE Mulch Film

作　　者：周艺峰[1] 聂王焰[1] 沙鸿飞 

机构地区：[1]安徽大学高分子材料研究所

出　　处：《塑料工业》1998年第4期116-118,共3页China Plastics Industry

基　　金：安徽省八五攻关项目

摘　　要：采用复合光敏剂并添加改性淀粉的方法，制备出降解诱导期可控的光和生物双降解聚乙烯地膜。地膜的力学性能符合ＧＢ１３７３５－９２标准，在田间曝露４０天左右后出现崩裂，强度急剧下降且呈突变性，经四个月后粘均分子量已降至５０００以下。真菌抗性试验表明此时的残膜易被土壤微生物侵蚀。采用红外光谱法对地膜降解过程中的化学结构变化进行了考察。Photobiodegradable PE mulch films,the degradation induction period of which was controllable,were prepared by adding compound photosensitizer with modified starchThe mechanicla properties of the films were　accord with GB1373592Exposed at field for about 40 days,the films split and the mechanical properties of the films decreased rapidly and abruptlyThe η of the films decreased to 5000 below after 4 monthsThe results of fungusresistant test showed the residue of the films was easily eroded by microorganism in the soilThe change of the chemical structure of the film during the degradation process was studied by means of IR spectrum

关 键 词：聚乙烯 光降解 生物降解 光敏剂 农用薄膜 

分 类 号：TQ325.12[化学工程—合成树脂塑料工业]