A1—Cu合金凝固过程中准固态力学性能及微量元素的影响  

MECHANICAL PROPERTIES OF QUASI-SOLID Al-Cu ALLOY AND INFLUENCE OF TRACE ELEMENTS DUING SOLIDIFICAfION

作　　者：魏晓伟[1] 曾明[1] 吴学婷[1] 

机构地区：[1]四川工业学院材料科学与工程系,成都611744

出　　处：《金属学报》1998年第7期719-724,共6页Acta Metallurgica Sinica

摘　　要：采用自制实验装置研究了A1—5％Cu合金在凝固过程中的准固态强度、强度增长率、断裂应变以及B，Ti，盐类细化剂和富Ce混合稀土对合金准固态力学性能的影响．研究结果表明，合金的准固态区即热脆性区，B，Ti和稀土都能降低合金准团相线温度，提高强度增长率和准固相线附近的强度，稀土的作用强于B和Ti．合金的中添加盐类细化剂后。The increase rate of strength, range of quasi-solid and failure strain of quasi-solid A1-5%Cu alloy during soliamcation are investigated with special apparatus. The influence of B,Ti, salt-refiner and mischmetal on the mechanical properties is also studied. Results obtained show that the range of quasi-solid is equivalent to the range of hot brittleness, and B, Ti as well as mischmetal all lower the quasi-solidus and enhance the strength around solidus and the increase rate of strength of the alloy. The effect of mischmetal is greater than that of B, Ti.Salt-refiner decreases the strength of quasi-solid and the failure strain of the alloy.

关 键 词：准固态 力学性能 微量元素 铝合金 凝固 

分 类 号：TG111.4[金属学及工艺—物理冶金] TG146.21[金属学及工艺—金属学]