配方及工艺对铁氧体材料综合性能的影响  

Formula and craft to ferrites material performance influence

作　　者：孙文婷[1] 陈存华[1] 王丽霞[1] 谢光远[2] 王齐军[2] 

机构地区：[1]华中师范大学化学学院,武汉430079 [2]武汉科技大学冶金与材料学院,武汉430021

出　　处：《华中师范大学学报（自然科学版）》2009年第2期267-269,共3页Journal of Central China Normal University：Natural Sciences

基　　金：湖北省自然科学基金项目(2007ABA058)

摘　　要：采用氧化物法制备了Mn-Zn铁氧体。利用X射线衍射仪(XRD)和扫描电子显微镜(SEM)观察烧结体显微结构。分析了配方中Fe、Mn、Zn的比例对铁氧体起始磁导率的影响及加工条件引起的烧结体密度变化。结果表明:缺铁配方更有利于改善铁氧体的磁性能,提高其起始磁导率。同时,采用预烧温度950℃、球磨时间5 h、成型压力50 MPa可使烧结体内部气孔减少、密度达到较好水平。The Mn-Zn ferrites were prepared by the oxide compound law. The sintered body microstructures were observed by the X-ray diffraction and scanning electronic microscope （SEM）. In the formula Fe, Mn the Zn proportion to influence the ferrites outset magnetic conductivity, and volume density changing with the working condition have been analyzed. The result indicated： The formula lacking Fe was more advantageous to the improvement ferrites magnetism performance, raises its outset magnetic conductivity. At the same time, uses the pre-fever temperature 950℃, ball grinding time 5 h, molding pressure 50 MPa to be possible to reduce the sintered body interior blowhole, and density is achieved to the good level.

关 键 词：MN-ZN铁氧体 显微结构 预烧温度 工艺条件 

分 类 号：TU52[建筑科学—建筑技术科学]