低活性渣体超高强高性能混凝土研究  

Investigation of super high-strength and high performance concrete containing low active slag

作　　者：李鸿芳[1] 刘翠然[1] 陈剑雄[2] 

机构地区：[1]洛阳理工学院土木工程系,河南洛阳471023 [2]重庆大学材料科学与工程学院,重庆400045

出　　处：《混凝土》2009年第8期43-46,共4页Concrete

摘　　要：研究了低活性超细石粉和钛渣对混凝土力学性能和抗Cl-渗透性的影响。掺加石粉可提高混凝土的强度,尤其是早期强度,3d强度在90MPa以上,7d强度超过了100MPa,其最佳掺量为10%左右。石粉与钛矿渣复掺,置换水泥量能达到40%,水泥用量减少到348kg/m3,28d强度超过了100MPa,仍能达到超高强混凝土的技术水平。混凝土的抗Cl-渗透能力随石粉掺量的增加而降低,随钛渣掺量的增加而提高。The influences of low active and super-fine limestone and titanium slag on the mechanical properties and Cl^- penetration resistance of concrete were investigated.The strength （especially for early strength） was remarkably improved by adding optimum 10% limestone, and it could reach 90 MPa after 3 days,and 100 MPa after 7 days,respectively.The amount of cement is reduced to 348 kg/m^3 after mixture of limestone and titanium slag was added, and 40% of cement was replaced.lts strength could reaches 100 MPa after 28 days,which is also on the level of high strength.Cl^- penetration resistance is degraded as addition of limestone increases,but the effect is converse for addition of titanium slag.

关 键 词：低活性渣体 超高强混凝土 力学性能 Cl-渗透性 

分 类 号：TU528.041[建筑科学—建筑技术科学]