固溶处理对2Al6铝合金显微组织和性能的影响  

The Influence of Different Solution Heat Treatment Processes on Microstructures and Mechanical Properties of 2Al6 Aluminum Alloy

作　　者：邓鹏辉[1,2] 张世兴[2] 

机构地区：[1]郑州大学,河南郑州450002 [2]河南工业大学,河南郑州450007

出　　处：《装备制造技术》2009年第9期36-38,共3页Equipment Manufacturing Technology

基　　金：河南省郑州市2007科技攻关基金资助项目(5-67)

摘　　要：研究了2Al6铝合金的固溶热处理工艺,分析了不同固溶热处理工艺对2A16铝合金显微组织和硬度的影响;结果表明,在经过525℃×10min固溶后,2A16铝合金能获得较好的固溶处理效果,为2A16铝合金后续热处理工艺参数的确定及优化提供了参考依据。In this paper different solution heat-treatment processes was researched and the influence of different solution heat-treatment processes on the microstruelures and hardness of the 2A16 aluminum alloy are analyzed. It is shown that the optimal solution heat-treatment process can be obtained at 525℃×10min, which can provide an evidence for the identification and optimization of parameters of heat-treatment process of the 2A16.

关 键 词：2A16铝合金 固溶处理 显微组织 硬度 