Fe_3O_4/聚苯胺纳米复合材料的吸波性能研究  

Study on Absorption Wave Property of Fe_3O_4/Polyaniline Nano-Composite Material

作　　者：贾瑛[1,2] 李志鹏[2] 张凌[2] 张秋禹[1] 

机构地区：[1]西北工业大学理学院,陕西西安710075 [2]第二炮兵工程学院503室,陕西西安710025

出　　处：《化学推进剂与高分子材料》2009年第5期33-37,共5页Chemical Propellants & Polymeric Materials

摘　　要：以磺基水杨酸(SSA)为乳化剂和掺杂剂,过硫酸铵(APS)为氧化剂,采用乳液聚合的方法合成了导电聚苯胺(PANI)包覆磁性四氧化三铁(Fe3O4)的纳米核-壳复合材料,并对纳米Fe3O4及复合材料进行了XRD、SEM、FT-IR表征。研究了Fe3O4/PANI纳米材料在2￣18GHz范围的微波电磁特性与吸波性能,结果表明:复合材料密度为0.12g/cm3时,其平均衰减为-5dB,最大衰减为-12dB,衰减为-5dB时的频宽可达6GHz。Core-shell nano-composite material of conducting polyaniline（PANI） coating Fe3O4（magnetic oxide） was synthesized by emulsion polymerization with sulfosalicylic acid（SSA） as emulsifying agent and dopant, and ammonium persulfate（APS） as oxidant. Nano-Fe3O4 and the composite material were characterized by XRD, SEM, FT-IR. Microwave electromagnetic characteristic and absorption wave property of Fe304/PANI were studied in the spectrum range of 2-18GHz. The results show that its average attenuation is -5 dB, maximum attenuation is -12dB, the band width can reach 6GHz at -5 dB when the density of the composite material is 0.12 g/cm^3.

关 键 词：磺基水杨酸 FE3O4 聚苯胺 吸波性能 

分 类 号：TB383.1[一般工业技术—材料科学与工程]