凝胶纺丝法制备超高分子量聚乙烯/高分子量聚乙烯纤维延伸性能的研究  

Investigation of the drawing behavior of gel fibers of ultrahigh molecular weight polyethylene/high molecular weight polyethylene blends

作　　者：李启成[1] 杨刚[1] 李雅明[1] 卢伟[1] 叶正涛[1] 

机构地区：[1]湖北大学材料科学与工程学院,武汉430062

出　　处：《胶体与聚合物》2009年第3期30-32,共3页Chinese Journal of Colloid & Polymer

摘　　要：用凝胶纺丝法制备了超高分子量聚乙烯(UHMWPE)/高分子量聚乙烯(HDPE)纤维,探讨了添加不同种类高分子量聚乙烯对凝胶初生纤维在后续延伸过程中延伸性能的影响。结果表明在固定制备条件时,当超高分子量聚乙烯(UHMWPE)/高分子量聚乙烯(HDPE)的质量比在最适当质量比时,高分子量聚乙烯的分子量为1.5～2.0×104时,所制备的凝胶初生纤维的可延伸比达最大值。The UHMWPE/HDPE fiber was produced using the gel spinning process. The influences of the different molecular weight polyethylene, on the drawing property of the originalfiber have been discussed in this paper. The result suggested that the draw ratio of the original fiber can reach the maximum value when the molecular weight of polyethylene was 1.5-2× 10^4, the weight proportion of UHMWPE/HDPE was 98：2.

关 键 词：凝胶纺丝法 初生纤维 延伸性能 高分子量聚乙烯 结晶 

分 类 号：TQ325.12[化学工程—合成树脂塑料工业] TQ342.87