Ti14合金半固态等温热处理过程中的组织演化规律  

Microstructure Evolution of Ti14 Alloy during Isothermal Process

作　　者：王慧[1] 陈永楠[1] 魏建锋[1] 赵永庆[2] 屈可朋[1] 

机构地区：[1]西安交通大学金属材料国家重点实验室,陕西西安710049 [2]西北有色金属研究院,陕西西安710016

出　　处：《稀有金属材料与工程》2009年第9期1533-1536,共4页Rare Metal Materials and Engineering

基　　金：重大基础研究前期研究专项项目(2005CCA06400);国家"973"项目(2007CB613807)

摘　　要：研究了Ti14合金在1000和1050℃半固态下,不同保温时间微观组织的演化过程,计算不同半固态温度下晶粒的生长指数,并分析半固态温度和保温时间对晶界和晶粒尺寸以及形态的影响规律。结果表明:随着保温时间的延长,晶粒明显长大,晶粒形态趋于圆整,晶界处液相由不连续分布转变为连续分布最终呈网格状;1000和1050℃对应的晶粒生长指数分别为0.88和0.97,表明温度的升高加速了微观组织的演化。Microstructure evolution of Ti t4 （α ＋ Ti2Cu） alloy during isothermal process at different semi-solid temperatures was researched. It is found that both the semi-solid temperature and holding time would affect the morphology of grain boundary and the grain size. The grains grow obviously and the grain＇s shape becomes globular with increasing the holding time, the distribution of liquid on grain boundary changes from discontinuous to continuous to form a latticed structure finally. According to the statistic analysis of experimental data, the grain growth index is 0.88 and 0.97 at 1000 ℃ and 1050 ℃, respectively, indicating that the rising of isothermal temperature would accelerated the microstructure evolution

关 键 词：TI14合金 半固态 微观组织 晶粒生长指数 

分 类 号：TG156.9[金属学及工艺—热处理]