溶胶-凝胶法制备Ni-Al_2O_3太阳光热转换吸收薄膜:过渡金属筛选和还原  

Ni-Al_2O_3 solar thermal absorbing film prepared by sol-gel method:screening and reduction of the transition metals

作　　者：蒋家兴[1] 赵剑曦[1] 廖新焕[1] 李镇祥[1] 姜蓉[1] 

机构地区：[1]福州大学化学化工学院应用化学系,福建福州350108

出　　处：《功能材料》2009年第10期1685-1687,共3页Journal of Functional Materials

基　　金：福建省青年人才创新基金资助项目(2008F3058)

摘　　要：针对溶胶-凝胶法制备太阳光热转换吸收薄膜的关键问题,筛选了过渡金属盐并考察了还原条件,结果表明不需要外加还原剂,直接利用溶胶配方组分就可以将硝酸镍完全原位还原成单质镍。配方中镍含量为80%(m(镍)∶m(铝)=80∶20)时获得最好的吸收率,灼烧温度以600℃为宜。依据这样条件,0.8mol/L溶胶制备的太阳光热转换吸收薄膜吸收率可达0.82。To the key question for sol-gel derived solar absorbing films,the transition metallic salts were filtratied out and the reduction condition was investigated. The results showed that nickel nitrate was reduced into elementary nickel by the sol formula without adding any other reducing agents. The best absorptance was obtained at 80% nickel content （m（Ni） ： re（Al） =80 ： 20）. The sintering temperature was determined at 600℃. By these conditions,the prepared film using 0.8mol/L sol has a normal solar absorbtance of 0.82.

关 键 词：太阳光吸收 Ni-Al2O3复合薄膜 过渡金属 盐筛选和还原 

分 类 号：TB331[一般工业技术—材料科学与工程] O611.3[理学—无机化学]