45钢轴件的性能分析  

Analysis on Properties of 45 Steel Axis

作　　者：刘丽霞[1] 李友荣[2] 

机构地区：[1]苏州市产品质量监督检验所,江苏苏州215128 [2]南京理工大学材料科学与工程系,江苏南京210094

出　　处：《物理测试》2009年第5期17-18,21,共3页Physics Examination and Testing

摘　　要：采用化学成分分析、硬度测试和金相检验等方法对45钢调质轴件的性能进行了分析。结果表明:由于锻造温度偏高,又未进行正火处理,造成了显微组织的异常,使得轴件的性能远不及正常的调质件,不能满足实际使用要求。The properties of the quenched and high temperature tempered 45 steel axis were analyzed by means of chemical analysis, hardness testing, and metallographic examination. The results showed that the microstructure of the 45 steel axis was abnormal, because the forging temperature was relatively high and the normalizing treatment was not conducted. Therefore, the properties of the workpiece were worse and could not satisfy the operation requirement.

关 键 词：调质 化学成分 硬度 显微组织 

分 类 号：TG115[金属学及工艺—物理冶金]