Evaluation of Oxidation of Ti-Al and Ti-Al-Cr Coatings Arc-ion Plated on Ti-60 High-temperature Titanium Alloy  

作　　者：Wei Yan Qingjiang Wang Jianrong Liu Shaoqiang Li Fengjiu Sun 

机构地区：[1]College of Sciences, Northeastern University, Shenyang 110004, China [2]Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

出　　处：《Journal of Materials Science & Technology》2009年第5期637-644,共8页材料科学技术（英文版）

摘　　要：High-temperature titanium alloy for aeroengine compressor applications suffers from high-temperature oxidation and environmental corrosion, which prohibits long-term service of this kind alloy at temperatures above 600℃. In an attempt to tackle this problem, Ti-48Al （at. pct） and Ti-48Al-12Cr （at. pct） protective coatings were plated on the substrate of alloy Ti-60 by arc ion plating （ALP） method. Isothermal and cyclic oxidation tests were performed in static air at elevated temperatures. Phase composition, morphology of the coatings and distribution of elements were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive X-ray analysis （EDX）. The results showed that the Ti-48Al coating exhibited good isothermal oxidation resistance during exposure at 800℃, but poorer resistance against oxidation at 900℃. By contrast Ti-48Al-12Cr coating demonstrated excellent isothermal oxidation resistance at both temperatures. Cyclic oxidation tests performed at 800℃ indicated that resistance and no spallation of coatings was observed. But both coatings demonstrated good cyclic oxidation at 900℃ only Ti-48Al-12Cr coating demonstrated excellent cyclic oxidation resistance.High-temperature titanium alloy for aeroengine compressor applications suffers from high-temperature oxidation and environmental corrosion, which prohibits long-term service of this kind alloy at temperatures above 600℃. In an attempt to tackle this problem, Ti-48Al （at. pct） and Ti-48Al-12Cr （at. pct） protective coatings were plated on the substrate of alloy Ti-60 by arc ion plating （ALP） method. Isothermal and cyclic oxidation tests were performed in static air at elevated temperatures. Phase composition, morphology of the coatings and distribution of elements were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive X-ray analysis （EDX）. The results showed that the Ti-48Al coating exhibited good isothermal oxidation resistance during exposure at 800℃, but poorer resistance against oxidation at 900℃. By contrast Ti-48Al-12Cr coating demonstrated excellent isothermal oxidation resistance at both temperatures. Cyclic oxidation tests performed at 800℃ indicated that resistance and no spallation of coatings was observed. But both coatings demonstrated good cyclic oxidation at 900℃ only Ti-48Al-12Cr coating demonstrated excellent cyclic oxidation resistance.

关 键 词：OXIDATION Ti-48Al coating Ti-48Al-12Cr coating High temperature titanium alloy 

分 类 号：TG146.23[一般工业技术—材料科学与工程] TQ055.81[金属学及工艺—金属材料]