溶液组分对铝阳极氧化多孔膜界面电性能的影响  

Influence of Electrolytes to the Interfacial Electroc Characteristics of the Porous Membrane of Anodized Aluminum

作　　者：旷亚非[1] 王玲[1] 王美媛[1] 

机构地区：[1]湖南大学化学化工学院

出　　处：《电化学》1998年第3期293-297,共5页Journal of Electrochemistry

摘　　要：采用电渗法研究了电解质溶液组分对铝阳极氧化多孔膜层界面电性能的影响．结果表明，多孔膜分别经含Ｆ－、ＰＯ３－４、ＳｉＯ２－３或单宁酸溶液浸泡处理后，膜在０．０１ｍｏｌ／ＬＫＣｌ溶液中的等电点由原来的ｐＨＩＥＰ＝９．２０分别移至ｐＨＩＥＰ＝３．４０，４．３０，３．３０和４．５０；ｐＨ＜ｐＨＩＥＰ时，多孔膜荷正电，ｐＨ＞ｐＨＩＥＰ时多孔膜荷负电，膜的ζ电位—ｐＨ曲线也发生了变化．经酸性品红和碱性品红溶液浸泡后的多孔膜，在２．０＜ｐＨ＜１１．０范围无等电点，膜的ζ电位始终大于零（碱性品红浸泡），ζ电位始终小于零（酸性品红浸泡）．The influence of electrolytic composition on the interfacial electric Characteristic of the porous membrane membrance of anodized aluminum was investigated with a electrodialytic method. Results indicated that, when the porous membrane was pretreated with F -, PO 3- 4,SiO 2- 3 and tannic acid, the isoelectric point in 0.01 mol/L KCI, were shifted from normal 9.20 to 3.40, 4.30, 3.30 and 4.50, respectively, and responsive characteristics of ζ potential to pH was changed. Furthermore, after pretreatment of porous membrance with fuchsine basic and fuchsine acid solution,there was no isoelectric point at 2.0<pH<11.0, and the ζ potentials were positive and negative, respectively.

关 键 词：铝 阳极氧化 界面电性能 多孔膜 

分 类 号：O614.31[理学—无机化学] O646.542[理学—化学]