Mg含量对Al-5%Cu合金凝固组织细化作用的研究  

Effects of Mg on Solidification Structure Refinement of Al-5%Cu Alloy

作　　者：何力佳[1] 王建中[1] 王春波[1] 曹丽云[1] 

机构地区：[1]辽宁工业大学材料与化学工程学院,辽宁锦州121001

出　　处：《热加工工艺》2009年第19期1-3,6,共4页Hot Working Technology

基　　金：辽宁省科技厅博士科研启动基金资助项目(20081097);国家自然科学基金资助项目(50674054)

摘　　要：系统地研究了不同Mg含量对Al-5%Cu合金凝固组织及性能的影响。结果表明:Mg元素对Al-5%Cu合金晶粒有细化作用,当Mg含量(质量分数)为0.8%时,细化效果较好,晶粒尺寸为0.912mm,二次枝晶间距为42.9μm,显微硬度值为74.16HV0.025,在磨损实验中合金失重较少,即抗磨损能力较强。To improve the property of Al-5%Cu alloy, the effects of Mg element on Al-5%Cu alloy solidification structure were studied. The results show that Mg has refinement on the solidification structure of Al-5%Cu alloy and can increase the matrix microhardness and anti-wear property, when the Mg content is 0.8%, the grain refinement is better relatively, the grain size is 0.912 mm, the secondary dendrite space is 42.9 μm, the matrix microhardness is 74.16HV0.025.

关 键 词：铝铜合金 凝固组织 细化 