改性丙烯酸树脂钢结构防火涂料制备研究  

Preparation of Modified Acrylic Resin Fire Retardant Paint on Steel Structures

作　　者：张爱黎[1] 张发余[1] 高虹[1] 刘万鹏[1] 

机构地区：[1]沈阳理工大学环境与化学工程学院,辽宁沈阳110168

出　　处：《电镀与精饰》2009年第10期38-41,46,共5页Plating & Finishing

基　　金：辽宁省沈阳市科技局项目(1053090-2-06)

摘　　要：研究了以丙烯酸树脂为基料、三聚氰胺聚磷酸盐为脱水催化剂、季戊四醇为成炭剂、三聚氰胺为发泡剂,可膨胀石墨和Mg(OH)2纳米颗粒为复合阻燃剂的超薄型钢结构防火涂料。结果表明:可膨胀石墨与Mg(OH)2纳米颗粒具有协同作用,同时添加5%可膨胀石墨与1.5%Mg(OH)2,δ为1.80 mm时,涂料的t耐火达106 min。防火涂料的理化性能符合技术指标GB14907-2002的要求。The uhrathin fire-resistant coatings for steel structure is studied, in which acrylic resin as a base material, melamine poly phosphate （MPP） as a dehydration agent, pentaerythritol （PER） as a char agent, melamine （MEL） as a vesicant and expandable graphite and nano-sized magnesium hydroxide as a flame retardant. The results show that expanded graphite （EG） and magnesium hydroxide nanoparticles are of synergic effect; the fire resistance is 106 min when 5% of expandable graphite and 1.5% of nanosized Mg（OH） 2 are added and the film thickness is 1.80 mm. The physical and chemical properties meet the technical standard of GB14907-2002.

关 键 词：防火涂料 可膨胀石墨 改性 钢结构 

分 类 号：TQ630.4[化学工程—精细化工]