壳聚糖接枝丙烯酸吸水纤维的制备及性能  

Preparation and properties of the chitosan graft acrylic acid absorbent fiber

作　　者：徐德增[1] 李丹[1] 郭静[1] 栾宇[1] 

机构地区：[1]大连工业大学化工与材料学院,辽宁大连116034

出　　处：《大连工业大学学报》2009年第5期351-353,共3页Journal of Dalian Polytechnic University

摘　　要：在引发剂过硫酸铵的引发下,使丙烯酸在壳聚糖的大分子链上接枝聚合,制得壳聚糖接枝丙烯酸纤维,用戊二醛对纤维进行一定程度的交联;采用红外光谱仪对制得的纤维进行了结构表征;研究了反应条件对纤维性能的影响。结果表明,使纤维具有较好吸水性能的最佳工艺条件为:壳聚糖质量0.5 g,过硫酸铵与丙烯酸的摩尔比为1.5%,反应时间3 h,凝固浴无水乙醇和10%NaOH体积比为30∶70,此条件下得到纤维的吸水率为275.67 g/g。Acrylic acid grafted onto the chitosan chain was initiated with ammonium persulfate. After cross-linked with glutaraldehyde, a kind of novel fiber was prepared. The fiber structure was characterized by FT-IR. The optimum synthesis conditions are as follows： the mass of chitosan is 0. 5 g, the mol ratio of the ammonium persulfate and acrylic acid is 1.5%, the reaction time is 3 h, and the volume ratio of absolute alcohol and 10% sodium hydroxide is 30 ： 70. The best swelling ratio of the fiber is 275.67.

关 键 词：壳聚糖 丙烯酸 纤维 吸水性能 

分 类 号：TQ342.69[化学工程—化纤工业]