顺丁烯二酸酐固相接枝羟乙基纤维素的制备与性能  

Esterification of Maleic Anhydride onto Hydroxyethyl Cellulose in Solid State

作　　者：陈蓉[1] 易传斌[1] 吴宏[1] 郭少云[1] 

机构地区：[1]高分子材料工程国家重点实验室四川大学高分子研究所,四川成都610065

出　　处：《高分子材料科学与工程》2009年第10期132-134,138,共4页Polymer Materials Science & Engineering

基　　金：国家973项目(2005CB623800)资助

摘　　要：以N,N-二甲基甲酰胺(DMF)为增塑剂,在无催化剂和溶剂条件下制备了羟乙基纤维素(HEC)和顺丁烯二酸酐(MAH)的酯化产物。通过酸碱滴定法测定酯化率和酯化效率,对酯化反应工艺进行了考察。采用FT-IR表征了产物结构,证明反应主要由MAH酸酐开环和HEC羟基酯化实现,并通过广角X射线衍射(WAXD)和热重分析(TG)对产物进行了进一步研究。结果表明,酯化反应后HEC结晶结构没有明显变化,热稳定性有了较大提高,最大分解温度从268℃提高到300℃左右。The chemical modification of hydroxyethyl cellulose（HEC） with maleic anhydride in the absence of solvent and catalyzer was studied.The optimum condition of the reaction was determined by the results of esterification degree and efficiency through acid-base titration method.FT-IR was used to investigate structural development of HEC during the processing,and indicated the esterification mechanism.Further investigation on the esterification reaction product was studied through WAXD and TG analysis.The results show that thermal stability of esterification product is improved obviouly,maximum degradation temperature is raised from 268 ℃ to about 300 ℃,but the crystal structure doesn′t change obviously

关 键 词：羟乙基纤维素 顺丁烯二酸酐 酯化 固相反应 

分 类 号：TQ316.343[化学工程—高聚物工业]