激光冲击对金属材料机械性能的影响  

Effects of laser shocking on the mechanical properties of metals

作　　者：任乃飞[1,2] 杨继昌[1,2] 蔡兰[1,2] 张永康[1,2] 

机构地区：[1]江苏理工大学机械制造系 [2]南京大学声学所

出　　处：《激光技术》1998年第4期235-238,共4页Laser Technology

基　　金：国家教委博士点专项科研基金;机械工业部教育司科技基金

摘　　要：用高功率钕玻璃激光装置对铝合金２０２４Ｔ６２进行激光冲击处理，激光参数：脉冲宽度（ＦＷＨＭ）为３０ｎｓ，单脉冲能量为１６５～２７５Ｊ，功率密度为１．１～１．６ＧＷ／ｃｍ２。试验结果表明：激光冲击区的表面硬度提高４２％，激光冲击区表层的晶粒得到细化，并且大幅度地提高了铝合金的疲劳寿命，在９５％置信度下，激光冲击试件的中值疲劳寿命是未冲击试件的５．４～１４．５倍。The　high　power　density,neodymiumglass　laser　is　used　to　laser　shockprocess　aluminum　alloy　2024T62.Laser　parameters:the　duration(FWHM)　is　30ns,the　single　laser　pulse　energy　is　16.5　to　27.5J,the　power　density　is　1.1　to　1.6GW/cm2.The　test　results　show　that　the　hardness　of　laser　shocking　zone　is　increased　about　42%,the　surface　grains　of　laser　shocking　zone　are　fined　and　the　fatigue　life　of　aluminum　alloy　is　increased　significantly.With　95%　confidence,the　fatigue　life　of　laser　shockprocessing　specimens　is　5.4　to　14.5　times　larger　than　the　unprocessed　specimens.

关 键 词：激光冲击处理 机械性能 金属材料 疲劳寿命 

分 类 号：TG115.5[金属学及工艺—物理冶金] TG156.99[金属学及工艺—金属学]