退火温度和平整对冷轧热镀锌双相钢组织和性能的影响  

Effect of Annealing Temperature and Temper Rolling on Mechanical Property and Microstructure of Cold Rolled Hot DIP Galvanized Dual Phase Steel

作　　者：罗青[1] 赵征志[1] 徐刚[1] 赵爱民[1] 金光灿[1] 刘光明[1,2] 

机构地区：[1]北京科技大学冶金工程研究院,北京100083 [2]首钢技术研究院,北京100041

出　　处：《钢铁研究学报》2009年第10期33-37,共5页Journal of Iron and Steel Research

基　　金：十一五国家科技支撑计划(2006BAE03A06);北京市科技计划(D07010300700701)

摘　　要：本文在实验室试制了高强度冷轧热镀锌用双相钢,探讨了不同的退火温度和平整工艺对双相钢力学性能和组织的影响规律。研究表明:退火温度在800℃以上时,试制的低硅C-Mn-Cr系双相钢才能得到由铁素体和马氏体组成的性能优良的双相钢。平整工艺显著提高双相钢的屈服强度和屈强比,降低双相钢的延伸率,平整率小于1%时,有利于工业上得到综合性能良好的双相钢。High strength cold rolled hot galvanized dual phase steels were pilot produced in laboratory. The effect of different annealing temperatures and temper rolling parameters on the mechanical properties of dual phase steels had been studied. The results show that when the annealing temperature is higher than 800 ℃ the microstructure of low Si C-Mn-Cr system dual phase steel is composed of ferrite and martensite, and the general mechanical prop- erties is preferable. Temper rolling can remarkably improve the yield strength and YS/TS ratio of dual phase steel and decrease total elongation slightly. When the temper rolling elongation is below 1 %, the dual phase steel with excellent mechanical properties can be obtained for industry production.

关 键 词：双相钢 显微组织 性能 热镀锌 平整 

分 类 号：TG142.15[一般工业技术—材料科学与工程]