利用炼钢二次灰作脱硫剂的初步研究  

A Study on the Use of Secondary Dust in Steel -Makingas Absorbent for Flue Gas Desulfurization

作　　者：王泉增[1,2] 陈晋南[1,2] 薄以匀 齐金彦[1,2] 吕琳 

机构地区：[1]北京理工大学化工与材料学院 [2]北京劳动保护研究所

出　　处：《北京理工大学学报》1998年第5期656-659,共4页Transactions of Beijing Institute of Technology

摘　　要：研究利用炼钢二次灰作为脱硫剂的可能性，方法到炼钢厂定期采样，分析其主要成分及碱性物在不同ｐＨ值和不同搅拌时间下的浸出情况．结果二次灰碱性物含量（折合为ＣａＯ）高达５０．２％以上；定量二次灰的碱性物析出量随ｐＨ值的降低而升高（ｐＨ为５时可析出６５．０％以上），且析出很快（在ｐＨ为４～６时，仅２０ｍｉｎ即可析出５０．０％）．结论炼钢二次灰是很好的脱硫剂．Aim To stuty the possibility of using secondary dust in steel- making as absorbent for flue gas desulfurization ( FGD) . Methods Samples are periodically taken from the steel- making plants. Components and the utilization ratio of alkaline materials in the dust are analyzed under different pH values and times of stirring. Results The contents of alkaline materials in the dust can reach as high as 50.2% (when converted into equivalent calcium oxide) . The percentage of separa- tion of alkaline materials from the dust increases as pH value decreases ( > 65% at pH5) and the separation speed is fast ( 50% separation at pH4 ～ 6 within only 20 min). Conclusion The steel-making dust is a kind of useful absorbent for FGD.

关 键 词：烟气脱硫 炼钢 二次灰 脱硫剂 大气污染 

分 类 号：X511[环境科学与工程—环境工程] X701