高附着耐水煮玻璃漆的研制  

Development of high-adhesion and boiling water-resistant glass paint

作　　者：刘忠[1] 沈球旺[1] 周荣华[1] 崔岳崧[1] 

机构地区：[1]深圳市天健涂料科技开发有限公司,广东深圳518122

出　　处：《电镀与涂饰》2009年第11期47-50,共4页Electroplating & Finishing

摘　　要：合成了玻璃环氧底漆,讨论了附着力促进剂、树脂和固化剂种类及用量对涂料性能的影响。结果表明,以1.5%3–缩水甘油醚氧基丙基三甲氧基硅烷为附着力促进剂,以E-20环氧树脂为成膜物、腰果壳油改性酚醛胺为固化剂制成底漆,配合丙烯酸聚氨酯黑面漆,获得了高附着、耐水煮的玻璃漆。An epoxy primer used on glass was synthesized, and the effects of categories and dosages of adhesion promoters, resins and curing agents were discussed. The results showed that a glass paint with high adhesion and boiling water resistance is obtained when acrylic polyurethane black top paint is combined with the primer prepared with 1.5% of 3-glycidoxypropyltrimethoxysilane as adhesion promoter, E-20 epoxy resin as film-forming material and cashew nut oil modified phenolic aldehyde amine as curing agent.

关 键 词：玻璃漆 环氧树脂 附着力 耐水煮性 

分 类 号：TQ630.7[化学工程—精细化工]