AZ91D镁合金的热压缩变形行为  

Compression deformation behavior of AZ91D magnesium alloy at elevated temperature

作　　者：张晓华[1] 姜巨福[1] 罗守靖[1] 

机构地区：[1]哈尔滨工业大学材料科学与工程学院,哈尔滨150001

出　　处：《中国有色金属学报》2009年第10期1720-1725,共6页The Chinese Journal of Nonferrous Metals

基　　金：国家自然科学基金资助项目(50605015);中国博士后基金资助项目(20060400812)

摘　　要：在应变速率为0.005～1s-1、温度250～350℃条件下,采用Instron-5500热模拟机对AZ91D镁合金的高温压缩特性进行研究,得到其真实应力—应变曲线。分析挤压温度和应变速率等对曲线的影响,得出本构方程的一系列常数,建立AZ91D镁合金在高温压缩中的本构方程关系式。结果表明:变形过程中AZ91D镁合金的流动应力随温度的升高而降低,随应变速率的升高而升高;该流动应力可以用双曲正弦函数来描述,其双曲正弦值随Zener-Hollomon参数自然对数的升高呈线性增大;AZ91D镁合金是正应变速率敏感材料,其应变速率敏感指数m=0.14。The compression tests of AZ91D magnesium alloy at elevated temperature were carried out on Instron-5500 at strain rates ranging from 0.005 to 1 s^-1 and deformation temperate between 250 and 350 ℃. The true stress-strain curves were obtained and the influences of deformation temperature and strain rate on the curves were analyzed. The constitutive equation and some constants of AZ91D magnesium alloy during compression deformation were gained. The results show that during the compression, the flow stress of AZ91D magnesium alloy decreases with increasing deformation temperature whereas it increase with increasing strain rates. The flow stress of AZ91D magnesium alloy at elevated temperature can be described with the hyperbolic sine function, and the hyperbolic sine value of flow stress will increase linely with increasing natural logarithm of Zener-Hollomon parameter. The strain rate sensitivity index （m） of AZ91D magnesium alloy is equal to 0.14.

关 键 词：AZ91D镁合金 高温压缩 流变应力 ZENER-HOLLOMON参数 

分 类 号：TG146.2[一般工业技术—材料科学与工程]