Austenite grain size and hardenability of Nb-B microalloyed gear steels

作　　者：马莉[1] 王毛球[1] 徐香秋[2] 王连海 赵亚平[4] 董瀚[1] 

机构地区：[1]钢铁研究总院先进钢铁材料技术国家工程研究中心,北京100081 [2]中国第一汽车集团公司技术中心,吉林长春130011 [3]抚顺特殊钢股份有限公司,辽宁抚顺113001 [4]宝山钢铁股份有限公司特殊钢分公司制造部,上海200940

出　　处：《材料热处理学报》2009年第5期74-78,91,共6页Transactions of Materials and Heat Treatment

基　　金：国家"863"计划(2006AA03Z526)

摘　　要：研究了Nb-B微合金化20CrMoH渗碳齿轮钢的奥氏体晶粒长大规律及微合金化对其淬透性的影响。结果表明,添加0.04%Nb可以有效地细化奥氏体晶粒,并且在1050℃奥氏体化10h无混晶现象。此外,添加0.0008%B能够明显提高钢的淬透性,使淬透性不因晶粒细化及Nb(C,N)析出而降低。Influence of Nb-B microalloying on austenite grain growth and hardenability of carburized gear steel 20CrMoH was investigated.The results indicate that austenite grain size can be refined effectively by adding 0.04%Nb in 20CrMoH steel and no abnormal growth of austenite grains is observed after austenitizing at 1050℃ for 10 h.In addition,the hardenability can be increased obviously by adding 0.0008% B into the steel,which can prevent hardenability from decreasing due to the grain refinement and Nb（C,N） precipitation.

关 键 词：齿轮钢 微合金化 晶粒尺寸 淬透性 

分 类 号：TG142.33[一般工业技术—材料科学与工程]