铜铝复合接触线用银铜合金的抗软化性和再结晶  

Softening and Recrystallization of Cu-Ag Alloy for Cu Cladding Al Contact Wire

作　　者：杨斌[1] 张迎晖[1] 孙洪波[1] 李明茂[1] 赵鸿金[1] 熊仕显[1] 

机构地区：[1]江西理工大学材料与化学工程学院

出　　处：《特种铸造及有色合金》2009年第11期991-993,共3页Special Casting & Nonferrous Alloys

基　　金：国家高技术研究发展计划(863计划)资助项目(2006AA03Z531);江西省2007年度科技支撑计划项目

摘　　要：研究了刚性铜铝复合接触线用银铜合金的抗软化性及再结晶,硬度测试、组织和静态再结晶动力学的分析结果表明,银铜合金的软化温度约为390℃,再结晶温度为350～450℃。银铜合金退火过程中发生再结晶的激活能为77.68kJ.mol-1;350℃、390℃退火时的再结晶完成时间分别约为414.4、167.7min。Softening and recrystallization of Cu-Ag alloy for Cu cladding Al contact wire were analyzed by hardness testing,microstructure and static recrystallization kinetics.The results indicate that softening temperature of the Cu-Ag alloy is approximately 390℃,and recrystallization temperature is in range of 350～450 ℃.Activation energy of recrystallization is calculated to be 77.68kJ/mol during annealing process.Completed time of recrystallization makes about 414.4,167.7 min with annealing at 350 ℃ and at 390℃.

关 键 词：铜铝复合接触线 银铜合金 退火 软化温度 再结晶 