The Role of Surfactant and Costabilizer in Controlling Size of Nanocapsules Containing TEGDMA in Miniemulsion  

作　　者：郭进新 黄翠 

机构地区：[1]School and Hospital of Stomatology,Wuhan University [2]Key Laboratory of Oral Biomedical Engineering of Ministry of Education,Wuhan University

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2009年第6期1004-1006,共3页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the National Natural Science Foundation of China (No.30672346)

摘　　要：Nanocapsules with triethylene glycol dimethacrylate （TEGDMA） as core material and polyurethane as wall material used for self-healing bonding resin were prepared by interfacial polycondensation in miniemulsion. The influence of surfactant and costabilizer concentration on nanocapsules size and stability of nanocapsules was investigated. The size and its polydispersity of the nanocapsules were measured by light-scattering particle size analyzer. When the concentration of SDS were increased from 2.5wt% to 10wt%,the size decreases from 340.5 nm to 258.3 nm, PDI decreased from 0.210 to 0.111. As the concentration of HD increased, the size and PDI were both decreased, When reaching 10wt%,the size was 258.0 nm,PDI was 0.130. SDS and HD play important effect in synthesis of Nanocapsules containing TEGDMA.By changing the surfactant and costabilizer concentration it was possible to synthesize a wide variety of nanocapsules sizes. The performance and technical parameters of nanocapsules had been researched preliminarily, which built the solid foundation for the application to the self-repairing bonding resin.Nanocapsules with triethylene glycol dimethacrylate （TEGDMA） as core material and polyurethane as wall material used for self-healing bonding resin were prepared by interfacial polycondensation in miniemulsion. The influence of surfactant and costabilizer concentration on nanocapsules size and stability of nanocapsules was investigated. The size and its polydispersity of the nanocapsules were measured by light-scattering particle size analyzer. When the concentration of SDS were increased from 2.5wt% to 10wt%,the size decreases from 340.5 nm to 258.3 nm, PDI decreased from 0.210 to 0.111. As the concentration of HD increased, the size and PDI were both decreased, When reaching 10wt%,the size was 258.0 nm,PDI was 0.130. SDS and HD play important effect in synthesis of Nanocapsules containing TEGDMA.By changing the surfactant and costabilizer concentration it was possible to synthesize a wide variety of nanocapsules sizes. The performance and technical parameters of nanocapsules had been researched preliminarily, which built the solid foundation for the application to the self-repairing bonding resin.

关 键 词：triethylene glycol dimethacrylate NANOCAPSULES interfacial polycondensation MINIEMULSION 

分 类 号：TB383.1[一般工业技术—材料科学与工程]