聚磷酸铵阻燃塑木复合材料的研究  

Research of Flame Retardanted Plastic-wood Composites by Ammonium Polyphosphate

作　　者：靳晓雨 王玉梅[2] 

机构地区：[1]大大科技集团研发中心 [2]惠东美新塑木型材制品有限公司

出　　处：《塑料制造》2009年第12期57-59,共3页Plastics Manufacture

摘　　要：以Ⅱ型聚磷酸铵为阻燃剂制备了阻燃塑木复合材料并通过水平燃烧、成炭量等评价了材料的综合性能。研究表明,APP的添加有效改善了塑木复合材料的水平燃烧性能,使材料的水平燃烧时间增加,水平燃烧速率下降。当APP的添加量为20%时,材料水平燃烧未烧至25mm处。塑木复合材料的成炭量较未添加时的23.7%,提高了一倍,氧指数提高了29%,表现出良好的阻燃性能。随着APP添加量的增加材料的拉伸强度和冲击强度有所下降,弯曲强度、弯曲模量则增加。The methods of horizontal burning, the amount of carbon residue and so on were used to evaluated properties of plastic-wood composites （WPC） flame retardanted by II-type ammonium polyphosphate. The test results showed that as the amount of APP adding, horizontal burning time increased and horizontal burning rate decreased. Adding 20% APP, the flame of WPC couldn＇t bum to 25mm. The carbon residue of WPC was doubled according to that 23.7% of WPC without flame retardant, LOI increased on 29%, showing good flame-retardant property. With the increase of the amount of APP, tensile strength and impact strength decreased, bending strength and bending modulus increased.

关 键 词：Ⅱ型聚磷酸铵塑木复合材料阻燃水平燃烧 

分 类 号：TQ327.9[化学工程—合成树脂塑料工业] TQ314.248