高效无机阻燃剂聚磷酸铵的合成  

Synthesis for ammonium polyphosphate of high efficiency inorganic flame retardant

作　　者：曹建喜[1] 罗立文[2] 郭冬冬[2] 田顺[2] 路来宾[2] 孔庆池[2] 徐春明[1] 

机构地区：[1]中国石油大学重质油国家重点实验室,北京102249 [2]中国石油大学化学化工学院,山东青岛266555

出　　处：《中国石油大学学报（自然科学版）》2009年第6期132-135,共4页Journal of China University of Petroleum(Edition of Natural Science)

摘　　要：通过实验对高聚合度聚磷酸铵的聚合条件进行优化,制备了平均聚合度为390的聚磷酸铵,考察物料配比、反应温度、反应气氛、反应时间、反应压力和处理温度、处理时间等对平均聚合度的影响。结果表明,n[(NH4)2HPO4]∶n(P2O5)∶n[CO(NH2)2]=1.0∶1.0∶0.3,湿氨气反应气氛,反应温度270℃,反应时间30 min,反应压力2.0 MPa,热处理温度250℃,热处理时间120 min为制备高聚合度的聚磷酸铵阻燃剂的最佳工艺条件。The polymeric conditions were optimized to prepare the ammonium polyphosphate （APP） with the average polymerization degree of 390. The effects of preparation conditions such as component proportion, reaction temperature, reaction atmosphere, reaction time, reaction pressure, treating temperature and treating time on the average polymerization degrees of APP were investigated. The following are the optimal technological conditions to prepare APP flame retardant of high polymerization degrees ： n[ （ NH4 ） 2 HPO4 ] ： n（ P2O5 ） ： n[ CO （ NH2 ） 2 ] = 1.0： 1.0： 0.3, reaction atmosphere of wet ammonia, reaction temperature of 270 ℃, reaction time of 30 min, reaction pressure of 2.0 MPa, treating temperature of 250 ℃, treating time of 10 min.

关 键 词：阻燃剂 聚磷酸铵 合成 制备 

分 类 号：O635.1[理学—高分子化学]