成核剂二-(3,4-二甲基苄叉)山梨醇在聚丙烯中的成核效应  被引量:6

Nucleation Effects of Nucleating Agent 1,3-O-2,4-Bis(3 ,4-Dimethylbenzylidene) Sorbitol in Isotactic Polypropylene

在线阅读下载全文

作  者:张跃飞[1] 李浔[1] 魏先善[1] 

机构地区:[1]长沙理工大学化学与生物工程学院,湖南长沙410004

出  处:《塑料》2009年第6期23-25,共3页Plastics

基  金:长沙理工大学校基金资助项目

摘  要:研究成核剂二-(3,4-二甲基苄叉)山梨醇(DMDBS)对等规聚丙烯力学性能、光学性能和结晶行为的影响。结果表明:DMDBS可以大幅度提高聚丙烯的力学性能、光学性能和结晶峰温度,具有很好的成核性能。当成核剂DMDBS添加浓度为0.2%时,与空白聚丙烯相比,成核聚丙烯的拉伸强度和弯曲模量可分别提高7.46%和11.96%,雾度可降低52.32%,结晶峰温度T_可从119℃左右提高到130℃左右。同时,DMDBS的加入可大幅度降低聚丙烯的球晶尺寸。Effects of 1,3-0-2,4-bis ( 3,4-dimethylbenzylidene ) sorbitol ( DMDBS ) on mechanical properties, optical properties and crystallization behaviors of isotactic polypropylene (iPP) were studied. The results showed that addition of DMDBS could increase the mechanical properties,optical properties and crystallization peak temperature of iPP greatly. When the addition concentration of DMDBS was 0. 2 % , compared to those of virgin iPP, tensile strength and flexural modulus of nucleated iPP could be increased by 7.46 % and 11.96 % , respectively, haze value could be decreased by 52.32 % and crystallization peak temperature( TC) could be increased from 119℃ to 130℃. At the same time, the addition of DMDBS could decrease spherulite size of iPP greatly.

关 键 词:成核效应 聚丙烯 二-(3 4-二甲基苄叉)山梨醇(DMDBS) 成核剂 结晶 

分 类 号:TQ325.14[化学工程—合成树脂塑料工业]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象