电磁搅拌对Mg-8Li-3Al合金显微组织和力学性能的影响  

Effects of Electromagnetic Stirring on Microstructure and Mechanical Properties of Mg-8Li-3Al Alloy

作　　者：马蕾娟[1] 郝海[1] 姚磊[1] 谷松伟[1] 董汉伟[1] 张兴国[1] 

机构地区：[1]大连理工大学材料科学与工程学院

出　　处：《特种铸造及有色合金》2009年第12期1144-1147,共4页Special Casting & Nonferrous Alloys

基　　金：教育部科学技术研究重点项目(107031);教育部新世纪优秀人才支持计划资助项目(NCET-08-0080)

摘　　要：研究了不同强度的电磁搅拌对Mg-8Li-3Al合金显微组织和力学性能的影响。结果表明,电磁搅拌能改善凝固过程的传热传质,细化枝晶,提高合金的抗拉强度、伸长率和硬度。当施加的电磁场电压为100V时,Mg-8Li-3Al合金的显微组织细小均匀,室温抗拉强度、伸长率和硬度(HB)分别达到212.9MPa、10.5%和71.3,合金的组织和力学性能达到最佳。Effects of electromagnetic stirring on microstructure and mechanical properties of Mg-8Li-3Al alloy were investigated.The results show that tensile strength,elongation and hardness of the alloy are obviously improved by electromagnetic stirring as a result of refining dendrite through improving heat transfer and mass transfer during solidification.With 100V electromagnetic voltage,ambient tensile strength,elongation and hardness of the Mg-8Li-3Al alloy with uniformly fine structure reach 212.9MPa,10.5% and 71.3,respectively.

关 键 词：电磁搅拌 Mg—Li—Al合金 显微组织 力学性能 

分 类 号：TG27[金属学及工艺—铸造]