化学组成对纤蛇纹石纳米管水热生长的影响  

Influence of Chemical Components on Hydrothermal Synthesis of Chrysotile Nano-tubes

作　　者：马国华[1] 彭同江[1] 李明[1] 

机构地区：[1]西南科技大学分析测试中心,四川绵阳621010

出　　处：《中国粉体技术》2009年第6期8-11,共4页China Powder Science and Technology

基　　金：国家自然科学基金项目;编号:40372030

摘　　要：以SiO_2和MgO为原料,研究了原料化学组成对纤蛇纹石纳米管生长的影响。采用水热法在不同n(SiO_2):n(MgO)比下合成了系列纤蛇纹石样品,利用X射线衍射(XRD)、红外光谱(FTIR)、扫描电镜(SEM)和透射电镜(TEM)对合成样品进行结构和形貌表征。结果表明:n(SiO_2):n(MgO)比偏离0.68不利于纤蛇纹石结构的生长;在n(SiO_2):n(MgO)比为0.68时,能够合成内径约为6～8 nm、外径约30～40 nm、长度多在600 nm以上的纤蛇纹石纳米管。The influence of molar ratio of SiO2 and MgO on the synthesis of ehrysotile nano-tubes was investigated. A series of chrysotile samples were synthesized from activated MgO and amorphous SiO2 by hydrothermal-reaction at different ratio ofn（SiO2） ： n（MgO）, X-ray diffraction, infra-red spectrometry, scanning electronic microscope and transmission electronic microscope were used to analyze the chrysotile samples. The resuits showed that the rate of formation of nano-tubes was determined by the rato value ofn （SiO2） ： n （MgO）. It was found that the tubed-stucture was easy to form, the erystallinity of chrysotile increased and its configuration becomed more clear as ratio value ofn （SiO2） ： n （MgO） reduced. As the ratio value of n（SiO2） ： n（MgO） was 0.68, the inner diameter for the chrysotile nano-tubes and the outer ones was 6-8 run and 30-40 nm and a length above 600 nm which was superior to other studies.

关 键 词：水热反应 纤蛇纹石纳米管 化学组成 

分 类 号：TH145.11[一般工业技术—材料科学与工程]