多层塑料复合板废料改性聚丙烯的研究  

Research on Polypropylene Modified by Waste Plastic Laminated Plates

作　　者：游长江[1] 曾一铮[1] 方旻[1] 李建雄[1] 

机构地区：[1]华南理工大学材料科学与工程学院,广东广州510640

出　　处：《中国塑料》2009年第12期77-81,共5页China Plastics

摘　　要：将用偶联剂和增容剂改性的多层塑料复合板固体废料粉末(GFRP)加入到聚丙烯(PP)基体中,制备复合材料。采用差示扫描量热仪、扫描电子显微镜研究了复合材料的微观结构和热性能,并测试了材料的力学性能。研究结果表明,当1%(质量分数,下同)硅烷偶联剂KH570处理的GFRP的含量为20份(质量份,下同),增容剂马来酸酐接枝聚丙烯(PP-g-MAH)含量为2份时,复合材料的冲击强度显著提高,弯曲强度与弯曲模量也有一定程度的提高,拉伸强度下降不大。扫描电子显微镜分析表明,PP/改性GFRP/PP-g-MAH复合材料在断裂过程中发生塑性变形,其韧性较好。差示扫描量热仪分析表明,GFRP的加入使材料的熔点略有下降。PP was filled with powder of waste plastic laminated plates（GFRP）, a coupling agents and a compatibilizer forming a composite, which was characterized using DSC, SEM, and the mechanical testings. When the contents of GFRP （modified by 1 wt % KH570） and the compatibilizer were 20 phr and 2 phr, respectively, the impact strength of the composites increased markedly, the flexural strength and modulus also increased based on neat PP. SEM indicated that plasticity deformation occurred during fracture process of the composite. DSC showed that the melting temperature decreased when adding GFRP into PP.

关 键 词：聚丙烯 多层塑料复合板 废料 改性 偶联剂 

分 类 号：TQ325.14[化学工程—合成树脂塑料工业]