LONG-TERM ATMOSPHERIC CORROSION BEHAVIOR OF LY12 ALUMINIUM ALLOY

作　　者：孙霜青[1] 郑弃非[1] 李德富[1] 陈杰[1] 温军国[1] 

机构地区：[1]北京有色金属研究总院,北京100088

出　　处：《中国腐蚀与防护学报》2009年第6期442-446,共5页Journal of Chinese Society For Corrosion and Protection

基　　金：国家自然科学基金项目(50499331);国家科技部基础条件平台建设项目(2005DKA10400-cj-2)资助

摘　　要：通过5种典型大气环境下为期20年的现场暴露试验,研究了LY12铝合金在我国长期大气腐蚀的规律和行为。结果表明,LY12在湿热的万宁和琼海分别暴露6年和10年后就发生了剥蚀,暴露20年后几乎丧失了力学性能,而在北京暴露20年后未出现剥蚀,仍保持良好的力学性能。LY12在大气污染物较多的江津和青岛腐蚀失重较大,在北京的腐蚀失重最小。剥蚀发生之前,LY12的腐蚀失重随暴露时间的变化遵循幂函数C=KT^n。剥落腐蚀产物中除Al屑之外主要为γ-Al(OH)_3和α-Al_2O_3·3H_2O。Atmospheric corrosion behavior of LY12 was investigated in five typical atmospheres in China over 20 years. Mass loss and loss in mechanical properties were measured; Appearance, cross-section photomicrograph and corrosion products were observed and analyzed by optical microscope and XRD. The results show that in hot and humid atmosphere of Wanning and Qioughai exfoliation corrosion occurred on LY12 after 6 and 10 years, respectively, and almost lost its mechanical properties after 20 years exposure. While in Beijing atmosphere, LY12 still performed excellent mechanical properties after 20 years exposure. The mass loss data were higher in Jiangjin and Qingdao due to higher average RH and SO2 or Cl^- contamination of the atmosphere, and lowest in Beijing atmosphere because of lower average RH. Before exfoliation corrosion occurred, the mass loss data with exposure time obeyed well with power function C=KT^n. The main exfoliation corrosion products are γ-Al（OH）3 and α-Al2O3·3H2O.

关 键 词：长期大气腐蚀 LY12 剥蚀 腐蚀失重 力学性能 

分 类 号：TG172.3[金属学及工艺—金属表面处理]