PVC/MOD合金蠕变行为研究  

Study on Creep Behavior of PVC/MOD Composite

作　　者：吴超[1] 吕洁[2] 吴广峰[1] 张会轩[1] 

机构地区：[1]长春工业大学合成树脂与特种纤维教育部工程研究中心,吉林长春130012 [2]中国石油吉林石化公司,吉林长春132021

出　　处：《广东化工》2010年第2期50-51,共2页Guangdong Chemical Industry

摘　　要：研究了聚氯乙烯/改性剂(PVC/MOD)合金在较小恒定外力,不同温度条件下的短期蠕变行为的时间相关性和温度相关性。通过PVC/MOD合金的短期蠕变行为,应用Findley方程预测了合金的长期蠕变行为。求得PVC/MOD合金在25、30和40℃作用应力为9 N时1.5年的形变率分别为3.3%,4.4%和54.4%。The PVC/modifier （PVC/MOD） composite of short-time creep behavior involved both time-dependent and temperature-dependent were investigated at a given lower stress and different temperature. Thus the long times creep behavior of PVC/MOD composite can be predicted from short-term were under Findley＇s power law model equation. For 1.5 years＇ experiment time, the results showed that the strain ratio was 3.3 %, 4.4 % and 54.4 % when temperature was 25, 30 and 40 ℃, respectively.

关 键 词：蠕变 时间相关性 温度相关性 Findley方程 