温压工艺对粘结NdFeB磁体性能的影响  

Effect of Warm Compaction Technology on Properties of Bonded NdFeB Magnets

作　　者：许启明[1] 尹丹凤[1] 赵旭东[1] 莫婵娟[1] 

机构地区：[1]西安建筑科技大学材料科学与工程学院,陕西西安710055

出　　处：《热加工工艺》2010年第2期27-28,31,共3页Hot Working Technology

摘　　要：采用温压工艺制备粘结NdFeB磁体,发现温压技术可以有效地提高粘结磁体的密度,改善磁体磁性能。研究表明:温压效果与温压温度的选择和温压压力密切相关。通过对温压机理的分析,发现最佳温压温度由粘结剂的软化点、粘度和固化点三个因素共同决定。而随着温压压力的升高,粘结NdFeB磁体的密度和磁性能增大,并在压力为650 MPa时得到了粘结磁体磁能积的最大值(50.43 kJ/m3)。Warm compaction was applied to prepare bonded NdFeB magnets. Warm compaction was proved to be a good way to improve the density and magnetic properties of bonded magnets. Studies show that the result of warm compaction is closely related with temperature and pressure. And softening point, viscosity and solidifying point of the bond decide the optimal temperature according to the mechanism of warm compaction. With the increase of warm compaction pressure, the density and magnetic properties of the bonded NdFeB magnets increase. And the bonded magnets with maximum best energy product （50.43 kJ/m^3） are obtained at the pressure of 650 MPa.

关 键 词：粘结NDFEB磁体 温压工艺 磁性能 

分 类 号：TM273[一般工业技术—材料科学与工程]