复合Zn/ZnS层的组织结构及其大气与真空环境下的摩擦学性能  

Microstructure and Tribological Properties of Zn/ZnS Layer in Air and Vacuum Environment

作　　者：司洪娟[1,2] 徐滨士[1] 王海斗[1] 马国政[1] 

机构地区：[1]装甲兵工程学院装备再制造技术国防科技重点实验室 [2]中国人民解放军93756部队

出　　处：《中国表面工程》2010年第1期75-79,共5页China Surface Engineering

基　　金：国家973计划(2007CB607601);北京自然科学基金(3072011);维修预研基金(9140A27030107OC85

摘　　要：采用纳米电刷镀技术在淬火后45钢表面制备Zn涂层,对其进行低温离子渗硫处理得到复合Zn/ZnS层。考察了该复合涂层在大气和真空环境下的减摩润滑性能。结果表明,高真空环境下,刷镀层孔隙有增多、变大现象。大气环境的摩擦试验过程中,暴露的新鲜涂层与大气中的氧作用形成氧化膜,导致磨损严重,润滑性能降低,摩擦因数在0.23左右。真空中的减磨润滑效果较好,摩擦因数相对较低,在0.18左右。Nano electro-brush plating was used to prepare Zn coating on the surface of quenched 1045 steel, and then the Zn coating was sulfurized to obtain Zn/ZnS composite layer. The tribological properties of the compound Zn/ZnS layer were investigated in air and vacuum atmosphere respectively. The results show that the pores of electro-brush plating layer became more and larger in high vacuum atmosphere. During the wear process in air, the exposed fresh coating acted with the oxygen in the atmosphere to generate an oxide film, resulting in the decline of lubricating property in the atmosphere. The friction coefficient in air was 0.23. In contrast, the lubricating effect in vacuum was superior, and the friction coefficient in vacuum was 0.18.

关 键 词：纳米电刷镀 低温离子渗硫 真空 摩擦学性能 

分 类 号：TG115.5[金属学及工艺—物理冶金] TB33[金属学及工艺—金属学]