Y_2O_3-ZrO_2陶瓷的电导特性研究  

Study on ionic conductivity property of Y 2O 3 ZrO 2 ceramic

作　　者：赵文广[1,2] 安立国 安胜利[1,2] 刘庆国 吴卫江[1,2] 

机构地区：[1]包头钢铁学院冶金与化学工程系 [2]北京科技大学理化系

出　　处：《包头钢铁学院学报》1998年第4期258-261,共4页Journal of Baotou University of Iron and Steel Technology

基　　金：冶金部人教司有偿与资助研究项目

摘　　要：对Ｙ２Ｏ３摩尔分数为６％的Ｙ２Ｏ３－ＺｒＯ２陶瓷的电导特性进行了实验研究．利用扫描电子显微镜、Ｘ光衍射仪、Ｖ氏硬度仪和交流阻抗法等研究测定了氧化钇部分稳定氧化锆在不同烧结温度下的显微组织、相比例、断裂韧性与电导率．实验证明，在温度为１６００℃时烧结的Ｙ２Ｏ３－ＺｒＯ２陶瓷材料，组织致密，其电导率达到１０－２Ｓ／ｃｍ，而四方相含量的降低可能是导致断裂韧性降低的重要原因．In the present, the ionic conductivity property of x(Y 2O 3)=6% Y 2O 3 ZrO 2 ceramic is studied by experiment. The microstructure, phase content, fracture toughness, ionic conductivity of Y 2O 3 ZrO 2 samples sintered at different sintering temperature is investigated by means of SEM, X-ray diffraction, Vicker's hardness apparatus and alternating electric resistance method. For the sample sintered at 1 600 ℃, the results demonstrate that the microstructure is dense, that the ionic conductivity amounts to 10 -2 S/cm and that the fracture toughness is decreased because the tetragonal phase ratio is decreased.

关 键 词：陶瓷 电导率 断裂韧性 氧化钇 氧化锆 

分 类 号：TQ174.758[化学工程—陶瓷工业]