纳米SiO_2材料的制备及其发光性能研究  

Preparation and luminescent properties of nanometer SiO_2

作　　者：郭艳[1] 王晓艳[1] 喻茹[1] 

机构地区：[1]成都理工大学材料与化学化工学院,成都610059

出　　处：《化工新型材料》2010年第2期76-78,共3页New Chemical Materials

摘　　要：采用溶胶-凝胶法制备了纳米SiO2,样品在800℃下煅烧2h。X-射线衍射（XRD）及扫描电子显微镜（SEM）测试结果表明,该材料具有非晶态结构,颗粒尺寸为90100nm。该样品在紫外灯照射下发出强烈的黄绿色可见光;对样品进行荧光光谱分析表明,该材料可以发射出较强的490nm的蓝绿光和弱的520nm的绿光。Nano-SiO2 luminescent materials were prepared by sol-gel technology.After calcined at 800℃ for 2hours,the structure of the samples was found to be amorphous with powder size between 90 and 100nm determined by X-ray diffraction and SEM.The samples were irradiated by UV light to send a strong yellow-green visible light.There were two luminescence bands at 490nm and at 520nm in the photoluminescence spectrum.And the light of 490nm were much stronger than the one of 520nm.

关 键 词：溶胶-凝胶法 纳米SIO2 发光性 

分 类 号：TB383.1[一般工业技术—材料科学与工程]