聚乙烯亚胺对ZnO纳米线阵列膜的形貌和光电性能的影响  

Effect of polyethylenimine on morphology and photovoltaic property of ZnO nanowire array films

作　　者：杨伟光[1] 万发荣[1,2] 姜春华 陈思维[1] 

机构地区：[1]北京科技大学材料科学与工程学院,北京100083 [2]北京市新能源材料与技术重点实验室,北京100083 [3]彩虹集团公司技术中心,北京100085

出　　处：《北京科技大学学报》2010年第1期78-82,共5页Journal of University of Science and Technology Beijing

摘　　要：采用X射线衍射仪、投射电镜仪和扫描电镜仪等测试手段,系统地研究了不同聚乙烯亚胺(PEI)浓度对ZnO纳米线阵列膜的形貌、线密度和尺寸的影响及ZnO纳米线阵列膜的光电性能.研究结果表明,在PEI浓度从3.2 mmol.L-1变化到9.3 mmol.L-1所制备的所有ZnO纳米线阵列膜中,使用7.3 mmol.L-1PEI浓度合成的ZnO纳米线阵列膜,制成染料敏化太阳能电池后获得0.66%的最高的光电转换效率.The effect of polyethylenimine（PEI） concentration on the morphology,wire density and size of ZnO nanowire arrays was systematically studied by X-ray diffraction（XRD）,transmission electron microscopy（TEM） and scanning electron microscope（SEM）.The photovoltaic properties of ZnO nanowire array films were also investigated.It is demonstrated that,for a ZnO nanowire array film obtained from 7.3 mmol·L-1 PEI,an energy conversion efficiency of about 0.66% was obtained,which is the highest for ZnO nanowire array films prepared with different PEI concentrations from 3.2 mmol·L-1 to 9.3 mmol·L-1.

关 键 词：纳米线阵列 光阳极 染料敏化太阳能电池 光电性能 

分 类 号：TB383[一般工业技术—材料科学与工程] TM914.4[电气工程—电力电子与电力传动]