新型梳状聚合物电解质的离子导电性 Ⅱ.侧链是分子量为550的聚乙二醇单甲醚  

IONIC CONDUCTIVITY OF NOVEL COMBLIKEPOLYMER ELECTROLYTEⅡ.Poly(ethylene glycol) methyl ether as side chains(M=550)

作　　者：齐力[1] 林云青[1] 景遐斌[1] 王佛松[1] 

机构地区：[1]中国科学院长春应用化学研究所

出　　处：《化学研究与应用》1998年第4期356-360,共5页Chemical Research and Application

摘　　要：以乙烯／马来酸酐共聚物为骨架，聚乙二醇单甲醚（Ｍ＝５５０）为侧链，通过两步酯化，合成了梳状乙烯／马来酸酐共聚物多缩乙二醇酯，用ＩＲ、元素分析、交流复阻抗谱等对产物及其ＬｉＣｌＯ４盐复合物进行了研究。结果表明：所合成的产物为非晶的梳状聚合物，并严格按反应方程式生成半酯。盐浓度与电导率的关系在所研究的浓度范围内存在两个峰，一峰在Ｏ／Ｌｉ＋＝８；另一峰在Ｏ／Ｌｉ＋＝３０。用侧链ＰＥＯ玻璃化转变温度作Ｔ０，以ｌｏｇσ对１／Ｔ－Ｔ０作图，电导率与温度关系呈典型的ＶＴＦ行为，该体系室温电导率最高可达２．５８×１０－５Ｓ／ｃｍ。おhe　SPEs　of　new　comblike　polymers　with　ethylenemaleic　anhydride　copolymer　as　backbone,oligooxyethylene　as　side　chains　were　synthesized　by　two　step　esterification　method.The　last　productions　and　its　LiClO4　complexes　were　charactrized　by　IR、elementary　analysis　and　impedance　technique.The　results　show　that　the　synthesized　products　are　noncrystallization,the　essential　reaction　was　complete　and　the　product　from　this　reaction　was　exactly　a　semiester.The　relation　between　conductivity　and　salt　concentration　in　the　studied　range　has　two　peaks,one　is　O/Li+=8　and　the　other　O/Li+=30.With　glass　transition　temperature　of　side　chain　as　T0,relation　between　conductivity　and　temperature　abides　VTF　behavior.The　conductivity　at　room　temperature　is　2.58×10-5S/cm.

关 键 词：梳状高分子 聚合物 固体电解质 SPE 聚环氧乙烷 

分 类 号：O633.11[理学—高分子化学] O631.23[理学—化学]