TiC和ZrC颗粒增强钨基复合材料  

Tungsten Matrix Composites Strengthened with TiC and ZrC Particles at Elevated Temperature

作　　者：宋桂明[1] 王玉金[1] 周玉[1] 雷廷权[1] 孙毅[1] 

机构地区：[1]哈尔滨工业大学材料科学与工程学院

出　　处：《固体火箭技术》1998年第4期54-59,共6页Journal of Solid Rocket Technology

摘　　要：用粉末冶金热压法制备ＴｉＣＰ／Ｗ和ＺｒＣＰ／Ｗ两种钨基复合材料，对其高温强度进行了研究，结果表明：随着温度提高，两种复合材料的抗弯强度开始时逐渐提高；当ＴｉＣＰ／Ｗ复合材料达到１０００℃时有最大值１１５５ＭＰａ，ＺｒＣＰ／Ｗ复合材料在８００℃时有最大值８２９ＭＰａ，分别比各自的室温强度提高５７％和１７％。而后，随温度的进一步提高，复合材料的强度又下降。分析了复合材料高温增强的机理。The investigation on the high temperature strength of these tungsten matrix composites,30%TiC P/W and 30%ZrC P/W fabricated by using powder metallurgy method involving hot pressing,shows that with increasing temperature,the flexural strength of these composites increased firstly,and as the temperature further increased,the strength of these composites decreased.The highest strength of TiC P/W composite was 1 155MPa reached at 1 000℃,which was 57% higher than that at room temperature,and the highest strength of ZrC P/W composite was 829MPa appeared at 800℃,which was 17% higher than that at room temperature.The strengthening mechanism at elevated temperature was given out.

关 键 词：金属基 复合材料 碳化钛 碳化锆 高温 

分 类 号：TB331[一般工业技术—材料科学与工程]