焊接工艺对药芯焊丝堆焊层中WC颗粒溶解行为的影响  

Influence of Surfacing Process on Dissolution of WC Particles in Surfacing Layers of Flux-cored Wires

作　　者：戴乐[1] 桂赤斌[1] 李连杰[1] 

机构地区：[1]海军工程大学船舶与动力学院,湖北武汉430033

出　　处：《热加工工艺》2010年第3期164-166,共3页Hot Working Technology

摘　　要：采用熔化极气体保护焊(MIG)、钨极氩弧焊(TIG)、氧乙炔火焰堆焊方法堆焊研制的WC耐磨堆焊药芯焊丝,研究了焊接工艺对堆焊层中WC颗粒溶解行为的影响。结果表明,堆焊方法的选择和电流大小对堆焊层中WC颗粒溶解行为有着重要影响。其中采用TIG连续焊和小电流MIG时,WC颗粒的溶解程度较轻。The developed WC flux-cored wires with wear resistance were deposited by MIG, TIG, oxyacetylene, the dissolution behavior of WC in the surfacing layers was investigated. The results show that the surfacing methods and current have a significant influence on the dissolution behavior of WC in the overlayers. Using TIG with continuing welding and MIG with small current have a little influence on the dissolution behavior of WC in the overlayers.

关 键 词：WC颗粒 堆焊 溶解 

分 类 号：TG455[金属学及工艺—焊接]