PP/PP-g-MAH/MMT纳米复合材料微孔发泡的研究  

Study on the microcellular foaming of the PP/PP-g-MAH/MMT nanocomposites

作　　者：高俊强[1,2] 何力[1,2] 张纯[2] 曹太山[1,2] 蒋团辉[1,2] 郝智[1,2] 

机构地区：[1]贵州大学,贵阳550003 [2]国家复合改性聚合物材料工程技术研究中心,贵阳550014

出　　处：《化工新型材料》2010年第3期100-102,共3页New Chemical Materials

基　　金：国家重点基础研究发展计划(973)项目(2007CB616912);贵州省科学技术基金项目(黔科合J字[2006]2110号)

摘　　要：通过熔融共混法制备聚丙烯/马来酸酐接枝聚丙烯/蒙脱土(PP/PP-g-MAH/MMT)纳米复合材料母粒。利用"二次开模"法注塑成型制得PP/PP-g-MAH/MMT纳米复合微孔发泡材料。研究了MMT和PP-g-MAH的用量对纳米复合微孔发泡材料发泡质量的影响。结果表明:5%的MMT和6%的PP-g-MAH有较好的协同效应,微孔发泡材料发泡倍率最大,泡孔平均直径最小,泡孔密度较大,泡孔尺寸分布范围较窄。The PP/PP-g-MAH/MMT nanocomposites were prepared by melt blending in two screw extruder.And the nanocomposite microcellular foams were made by ＂two times opening mold＂ injection molding method.The foaming quality of the PP/PP-g-MAH/MMT nanocomposites with varied contents of MMT and PP-g-MAH were investigated,respectively.The results indicated that the composite with 5% MMT and 6% PP-g-MAH had the best foaming quality.

关 键 词：聚丙烯 纳米蒙脱土 马来酸酐接枝聚丙烯 微孔发泡 泡孔直径 泡孔密度 